ApplicationAll building and glazing joints which require a fire rating.
Fire rated expansion joints.
Base: Polysiloxane
Consistency: Stable Pasta
Curing System: Moisture Cure
Skin Forming: Ca 20 min. (20C/65% R.H.)
Curing Rate 1mm/24h
Shore A Hardness: 16 Shore A
Specific Gravity: Ca 1,17g/cm
Temperature Resistance: -40C until +140C
Elongation at Break900% (DIN52455)
E-Modulus 100%0,20N/mm (DIN52455)Elastical Recovery>90% (DIN52455)Maximum Deformation25%
All building and glazing joints which require a fire rating.
Fire rated expansion joints.
Base: Polysiloxane
Consistency: Stable Pasta
Curing System: Moisture Cure
Skin Forming: Ca 20 min. (20C/65% R.H.)
Curing Rate 1mm/24h
Shore A Hardness: 16 Shore A
Specific Gravity: Ca 1,17g/cm
Temperature Resistance: -40C until +140C
Elongation at Break900% (DIN52455)
E-Modulus 100%0,20N/mm (DIN52455)Elastical Recovery>90% (DIN52455)Maximum Deformation25%
Silicone
Construction
MCcoy Soudal
Other
Trade Information
Ahmedabad
1-2 Unit Per Week
1-2 Week
Contact us for information regarding our sample policy
Gujarat
Product Description
FIRE SILICONE B1 FR
Applications:
All building and glazing joints which require a fire rating.